20CrMnTi齿轮钢的点蚀敏感性及裂纹萌生风险

余稳 向嵩 石维 马国强 于明飞

余稳, 向嵩, 石维, 马国强, 于明飞. 20CrMnTi齿轮钢的点蚀敏感性及裂纹萌生风险[J]. 工程科学学报, 2017, 39(5): 731-738. doi: 10.13374/j.issn2095-9389.2017.05.011
引用本文: 余稳, 向嵩, 石维, 马国强, 于明飞. 20CrMnTi齿轮钢的点蚀敏感性及裂纹萌生风险[J]. 工程科学学报, 2017, 39(5): 731-738. doi: 10.13374/j.issn2095-9389.2017.05.011
YU Wen, XIANG Song, SHI Wei, MA Guo-qiang, YU Ming-fei. Pitting sensitivity and crack initiation risk of 20CrMnTi gear steel[J]. Chinese Journal of Engineering, 2017, 39(5): 731-738. doi: 10.13374/j.issn2095-9389.2017.05.011
Citation: YU Wen, XIANG Song, SHI Wei, MA Guo-qiang, YU Ming-fei. Pitting sensitivity and crack initiation risk of 20CrMnTi gear steel[J]. Chinese Journal of Engineering, 2017, 39(5): 731-738. doi: 10.13374/j.issn2095-9389.2017.05.011

20CrMnTi齿轮钢的点蚀敏感性及裂纹萌生风险

doi: 10.13374/j.issn2095-9389.2017.05.011
基金项目: 

国家自然科学基金资助项目(51361004,51661006);贵州省百层次创新型人才资助项目(20164014);贵州省科技计划资助项目(20142003,20147603,20152031);贵州省教育厅创新群体重大研究资助项目(2016021);贵州大学人才基金资助项目(201448)

详细信息
  • 中图分类号: TG172.9

Pitting sensitivity and crack initiation risk of 20CrMnTi gear steel

  • 摘要: 利用弱腐蚀倾向的溶液环境,控制20CrMnTi钢产生有限的亚稳态蚀点分布.运用电化学噪声法,研究了20CrMnTi钢亚稳态蚀点的萌生规律,结合ANSYS有限元计算,导入真实腐蚀形貌,对比研究了不同腐蚀条件下蚀孔周边的应力分布与裂纹萌生风险.结果表明,20CrMnTi具有较高的点蚀敏感性,其亚稳态蚀点集中在杂质相边缘优先形核,随Cl-浓度的升高,点蚀孕育期明显缩短,点蚀敏感性增大.不同Cl-浓度下引起的形核速率上升会缩短蚀点间距,表面微裂纹易连接蚀点而发生扩展,增大裂纹萌生风险.
  • [3] Hou J, Song L. Numerical investigation on stress concentration of tension steel bars with one or two corrosion pits. Adv Mater Sci Eng, 2015, 2015:1
    [4] Elshawesh F, Elhoud A, Zeglam W, et al. Corrosion fatigue of Incoloy 825 flare gas line bellows of expansion joints. J Failure Anal Prevention, 2015, 15(1):7
    [5] Gabb T P, Telesman J, Hazel B, et al. The effects of hot corrosion pits on the fatigue resistance of a disk superalloy. J Mater Eng Performance, 2010, 19(1):77
    [6] Dolley E J, Lee B, Wei R P. The effect of pitting corrosion on fatigue life. Fatigue Fract Eng Mater Struct, 2000, 23(7):555
    [7] Bertocci U, Ye Y X. An examination of current fluctuations during pit initiation in Fe-Cr alloys. J Electrochem Soc, 1984, 131(5):1011
    [8] Qiao G F, Ou J P. Corrosion monitoring of reinforcing steel in cement mortar by EIS and ENA. Electrochim Acta, 2007, 52(28):8008
    [9] Okada T. A two-step initiation hypothesis of pitting corrosion in passive metals. Corros Sci, 1990, 31:453
    [10] Macdonald D D. The point defect model for the passive state. J Electrochem Soc, 1992, 139(12):3434
    [12] Dong Z H, Shi W, Guo X P. Initiation and repassivation of pitting corrosion of carbon steel in carbonated concrete pore solution. Corros Sci, 2011, 53(4):1322
  • 加载中
计量
  • 文章访问数:  434
  • HTML全文浏览量:  72
  • PDF下载量:  5
  • 被引次数: 0
出版历程
  • 收稿日期:  2016-08-04

目录

    /

    返回文章
    返回