Fe对金刚石刻蚀反应的相分析

Identification of Phases for Etching Interaction of Fe with Diamond

    摘要
  • 摘要: 研究了950 ℃保温6 min时Fe对金刚石的刻蚀反应.用AES微区成分分析给出了金刚石晶格中的C原子，自金刚石与Fe的相界面溶入Fe中的分布，并通过AESCKLL谱确认了溶入Fe中C的存在状态是石墨，而无碳化物相形成.

     

    Abstract: The etching interaction of Fe with diamond was studied after sintering at 950 ℃ for 6 min. According to the result of AES C KLL line, the state of carbon near the diamond-iron interface was determined to be considered as graphite but not Fe3C. Carbon atom is dissolved from diamond crystal lattice into iron.

     