Al-Ca复合合金钢水脱氧机理的研究

王晓英 仇圣桃 邹宗树 干勇

王晓英, 仇圣桃, 邹宗树, 干勇. Al-Ca复合合金钢水脱氧机理的研究[J]. 工程科学学报, 2017, 39(5): 702-709. doi: 10.13374/j.issn2095-9389.2017.05.008
引用本文: 王晓英, 仇圣桃, 邹宗树, 干勇. Al-Ca复合合金钢水脱氧机理的研究[J]. 工程科学学报, 2017, 39(5): 702-709. doi: 10.13374/j.issn2095-9389.2017.05.008
WANG Xiao-ying, QIU Sheng-tao, ZOU Zong-shu, GAN Yong. Study on steel deoxidation with Al-Ca compound alloy[J]. Chinese Journal of Engineering, 2017, 39(5): 702-709. doi: 10.13374/j.issn2095-9389.2017.05.008
Citation: WANG Xiao-ying, QIU Sheng-tao, ZOU Zong-shu, GAN Yong. Study on steel deoxidation with Al-Ca compound alloy[J]. Chinese Journal of Engineering, 2017, 39(5): 702-709. doi: 10.13374/j.issn2095-9389.2017.05.008

Al-Ca复合合金钢水脱氧机理的研究

doi: 10.13374/j.issn2095-9389.2017.05.008
详细信息
  • 中图分类号: TG142.71

Study on steel deoxidation with Al-Ca compound alloy

  • 摘要: 通过Al-Ca复合合金钢水脱氧的平衡热力学计算,确定了钢液的氧的质量分数在3×10-6~1×10-4条件下,1600℃时的Al-Ca复合合金脱氧产物的稳定区域图.以此为基础,假定钙的收得率为100%,预测了钢液在Al-Ca复合合金Ca/Al质量比为5,加入量为M kg;Al-Ca复合合金Ca/Al质量比为0.2,加入量为M kg;Al-Ca复合合金Ca/Al质量比为0.2,加入量为0.2M kg三种不同脱氧制度下夹杂物的演变历程.结果表明,在Ca/Al=5,复合合金加入量使初始钢液中的[Ca]为0.01%,[Al]为0.002%时,夹杂物在钢液精炼过程中的演变历程为:12CaO·7Al2O3(l)/CaO·Al2O3(l)→CaO (s)→12CaO·7Al2O3(l)/CaO·Al2O3(l)→CaO (s)→12CaO·7Al2O3(l)/CaO·Al2O3(l),并确定了固态和液态脱氧产物在脱氧过程中交替形成为最理想的Al-Ca复合合金脱氧制度,可为钢铁企业脱氧剂的选择和应用提供参考和借鉴.
  • [1] Fernandes M, Pires J C, Cheung N, et al. Influence of refining time on nonmetallic in a low-carbon, silicon-killed steel. Mat Charact, 2003, 51(5):301
    [2] Mintz B, Mohamed Z, Abu-Shosha R. Influence of calcium on hot ductility of steels. Mater Sci Technol, 1989, 5(7):682
    [6] Li Y, Wan X L, Lu W Y, et al. Effect of Zr-Ti combined deoxidation on the microstructure and mechanical properties of high-strength low-alloy steels. Mat Sci Eng A, 2016, 659:179
    [7] Kim H S, Chang C H, Lee H G. Evolution of inclusions and resultant microstructural change with Mg addition in Mn/Si/Ti deosidized steels. Mat Sci Eng A, 2005, 53(11):1253
    [8] Shibata H, Kimura K, Tanaka T, et al. Mechanism of change in chemical composition of oxide inclusions in Fe-Cr Alloys deoxidized with Mn and Si by heat treatment at 1473 K. ISIJ Int, 2011, 51(12):1944
    [12] Zhang T S, Min Y, Liu C J, et al. Effect of Mg addition on the evolution of inclusions in Al-Ca deoxidized melts. ISIJ Int, 2015, 55(8):1541
    [14] Hideaki S, Ryo I. Thermodynamics on control of inclusions composition in ultraclean steels.ISIJ Int, 1996, 36(5):528
  • 加载中
计量
  • 文章访问数:  450
  • HTML全文浏览量:  104
  • PDF下载量:  3
  • 被引次数: 0
出版历程
  • 收稿日期:  2016-07-27

目录

    /

    返回文章
    返回