6005A铝合金的表面损伤对其耐海水腐蚀性能的影响

何明涛 孟惠民 王宇超 任鹏伟

何明涛, 孟惠民, 王宇超, 任鹏伟. 6005A铝合金的表面损伤对其耐海水腐蚀性能的影响[J]. 工程科学学报, 2018, 40(1): 92-98. doi: 10.13374/j.issn2095-9389.2018.01.012
引用本文: 何明涛, 孟惠民, 王宇超, 任鹏伟. 6005A铝合金的表面损伤对其耐海水腐蚀性能的影响[J]. 工程科学学报, 2018, 40(1): 92-98. doi: 10.13374/j.issn2095-9389.2018.01.012
HE Ming-tao, MENG Hui-min, WANG Yu-chao, REN Peng-wei. Effect of surface damage on the corrosion resistance of 6005A aluminum alloy in simulated seawater[J]. Chinese Journal of Engineering, 2018, 40(1): 92-98. doi: 10.13374/j.issn2095-9389.2018.01.012
Citation: HE Ming-tao, MENG Hui-min, WANG Yu-chao, REN Peng-wei. Effect of surface damage on the corrosion resistance of 6005A aluminum alloy in simulated seawater[J]. Chinese Journal of Engineering, 2018, 40(1): 92-98. doi: 10.13374/j.issn2095-9389.2018.01.012

6005A铝合金的表面损伤对其耐海水腐蚀性能的影响

doi: 10.13374/j.issn2095-9389.2018.01.012
基金项目: 

国家重点基础研究发展计划(973计划)资助项目(2014CB643302)

详细信息
  • 中图分类号: TG172.5

Effect of surface damage on the corrosion resistance of 6005A aluminum alloy in simulated seawater

  • 摘要: 以6005A铝合金商品实际产生的表面少缺陷、多缺陷试样,以及作为比较的完全去除商品表面膜的人工磨制的三种不同表面状态试样为研究对象,研究铝合金商品表面的实际损伤对其耐海水腐蚀性能的影响及其腐蚀电化学行为.通过场发射扫描电镜和激光共聚焦扫描显微镜对具有不同表面状态的6005A铝合金表面形貌和粗糙度进行了表征,表明铝合金商品实际产生的表面缺陷主要为划伤,体现在随着表面缺陷的增多,表面粗糙度Ra明显增大,表面粗糙度Ra大小可以定量描述表面损伤的严重程度. 6005A铝合金在NaCl质量分数3.5%的模拟海水溶液中发生全面腐蚀和点蚀,表面缺陷越多,粗糙度越大,耐蚀性越差;电化学测试结果表明,表面缺陷越多,粗糙度越大,腐蚀电位越低,腐蚀电流密度越大,耐蚀性越差. 6005A铝合金表面损伤对其耐海水腐蚀性能产生影响的原因为:表面损伤造成铝合金商品原表面膜被破坏,表面缺陷越多,粗糙度越大,表面膜的破坏和表面塑性变形越严重,铝元素会因为被活化而迅速溶解,有着更高的腐蚀速率,而缺陷较少表面有较为均匀致密的氧化膜,对基体有着较好的保护性.
  • [2] Ji S D, Meng X C, Liu J G, et al. Formation and mechanical properties of stationary shoulder friction stir welded 6005A-T6 aluminum alloy. Mater Des, 2014, 62:113
    [3] Vyazovikina N V. The effect of scandium on the corrosion resistance of aluminum and its alloys in 3% NaCl solution. Prot Met, 1999, 35(5):448
    [5] Vargel C. Corrosion of Aluminum. Amsterdam:Elsevier, 2004
    [8] Schumacher M M. Sea Water Corrosion Handbook. New Jersey:Noyes Data Corp., 1979
    [9] Fadaee H, Javidi M. Investigation on the corrosion behaviour and microstructure of 2024-T3 Al alloy treated via plasma electrolytic oxidation. J Alloys Compd, 2014, 604:36
    [13] Acharyya S G, Khandelwal A, Kain V, et al. Surface working of 304L stainless steel:impact on microstructure, electrochemical behavior and SCC resistance. Mater Charact, 2012, 72:68
    [14] Large D, Sabot R, Feaugas X. Influence of stress-strain field on the dissolution process of polycrystalline nickel in H2SO4 solution:an original in situ method. Electrochim Acta, 2007, 52(27):7746
    [15] Ziemniak S E, Hanson M, Sander P C. Electropolishing effects on corrosion behavior of 304 stainless steel in high temperature, hydrogenated water. Corros Sci, 2008, 50(9):2465
    [16] Li W, Li D Y. Influence of surface morphology on corrosion and electronic behavior. Acta Mater, 2006, 54(2):445
    [18] Andreatta F, Terryn H, De Wit J H W. Corrosion behaviour of different tempers of AA7075 aluminium alloy. Electrochim Acta, 2004, 49(17-18):2851