高磷硅锰合金还原脱磷实验研究

周胜楠 朱子宗 周志强 梁洁旗 李东营

周胜楠, 朱子宗, 周志强, 梁洁旗, 李东营. 高磷硅锰合金还原脱磷实验研究[J]. 工程科学学报, 2018, 40(8): 931-936. doi: 10.13374/j.issn2095-9389.2018.08.006
引用本文: 周胜楠, 朱子宗, 周志强, 梁洁旗, 李东营. 高磷硅锰合金还原脱磷实验研究[J]. 工程科学学报, 2018, 40(8): 931-936. doi: 10.13374/j.issn2095-9389.2018.08.006
ZHOU Sheng-nan, ZHU Zi-zong, ZHOU Zhi-qiang, LIANG Jie-qi, LI Dong-ying. Experimental research on the dephosphorization of high phosphorus Si-Mn alloy[J]. Chinese Journal of Engineering, 2018, 40(8): 931-936. doi: 10.13374/j.issn2095-9389.2018.08.006
Citation: ZHOU Sheng-nan, ZHU Zi-zong, ZHOU Zhi-qiang, LIANG Jie-qi, LI Dong-ying. Experimental research on the dephosphorization of high phosphorus Si-Mn alloy[J]. Chinese Journal of Engineering, 2018, 40(8): 931-936. doi: 10.13374/j.issn2095-9389.2018.08.006

高磷硅锰合金还原脱磷实验研究

doi: 10.13374/j.issn2095-9389.2018.08.006
基金项目: 

国家自然科学基金资助项目(51774054)

详细信息
  • 中图分类号: TF642.3

Experimental research on the dephosphorization of high phosphorus Si-Mn alloy

  • 摘要: 在硅钼炉中,1400℃的条件下,利用硅钙合金、稀土硅、铝基脱磷剂等对高磷硅锰合金进行还原脱磷实验研究.脱磷实验采用CaO-CaF2(质量比为25∶75)为覆盖渣,渣金比为0.2∶1.采用ICP光谱仪检测脱磷后合金中的磷含量,X射线衍射检测渣样物相成分,着重分析了不同脱磷剂及其用量对高磷硅锰合金还原脱磷的影响.结果表明:随脱磷剂用量的增加,硅锰合金脱磷率呈上升的趋势.其中,铝基脱磷剂脱磷效果最好,当其质量分数达到8%时,合金中磷的质量分数可降至0.21%,符合国标要求(≤ 0.25%),脱磷率达78%;硅钙合金次之,当其质量分数达到10%时,脱磷率为47%;稀土硅的脱磷效果最差,当其质量分数达10%时,脱磷率仅22%.铝基脱磷剂为本实验条件下的最佳脱磷剂.
  • [1] Song Q, Zhao Y, Zhu J. Dephosphorization of manganese ore by high-intensity magnetic separation and roast-leaching. Trans Inst Min Metall Sect C, 1989, 98:C17
    [2] Kanungo S B, Mishra S K. Dephosphorization of high-phosphorus manganese ores of southern Orissa and Andhra Pradesh, India, by roasting with sodium chloride followed by leaching in dilute nitric acid. Miner Process Extr Metall, 2013, 109(3):C145
    [4] Zhu L J, Wu D, Zhao X M. Effect of silicon content on thermodynamics of austenite decomposition in C-Si-Mn TRIP steels. J Iron Steel Res Int, 2006, 13(3):57
    [5] Tabuchi S, Sano N. Thermodynamics of phosphate and phosphide in CaO-CaF2 melts. Metall Trans B, 1984, 15(2):351
    [6] Shin J H, Park J H. Thermodynamics of reducing refining of phosphorus from Si-Mn alloy using CaO-CaF2 slag. Metall Mater Trans B, 2012, 43(6):1243
    [7] Masumitsu N, Ito K, Fruehan R J. Thermodynamics of Ca-CaF2 and Ca-CaCl2 systems for the dephosphorization of steel. Metall Trans B, 1988, 19(4):643
    [11] Meteleva-Fischer Y, Yang Y, Boom R, et al. Alloying refining of metallurgical grade sillicon with rare earth elements//TMS 2013. Texas, 2013:201
    [12] Tang K, Løvvik O M, Safarian J, et al. Removal of phosphorus in metallurgical silicon by rare earth elements. Metall Mater Trans E, 2014, 1(3):257
    [14] Ban B Y, Bai X L, Li J W, et al. The mechanism of P removal by solvent refining in Al-Si-P system. Metall Mater Trans B, 2015, 46(6):2430
  • 加载中
计量
  • 文章访问数:  470
  • HTML全文浏览量:  83
  • PDF下载量:  4
  • 被引次数: 0
出版历程
  • 收稿日期:  2017-09-15

目录

    /

    返回文章
    返回